Definition:

• Two-Part HS Mixed Filler -LGF 810 150 A4-, white
• Two-Part HS Mixed Filler -LGF 810 151 A4-, black
• Two-Part HS Mixed Filler -LGF 810 152 A4-, red
• Two-Part HS Mixed Filler -LGF 810 153 A2-, yellow
• Two-Part HS Mixed Filler -LGF 810 154 A2-, blue
• Two-Part HS Mixed Filler -LGF 810 155 A2-, green

Product Description

The two-part HS mixed filler system is part of the latest generation of innovative color two-part acrylic-resin-based HS filler systems.

The system consists of 6 colored fillers (white, black, yellow, red, green, blue). These fillers can also be mixed together with the aid of simple formulas.

All settings of this product are VOC compliant.

Properties:

1. can be used as an interior color and as a "wet-in-wet" filler
   • Excellent, simple and variable processing options
   • Flows well
   • Very quick drying performance
   • Very nice paint finish
   • Great stability under load
   • High yield
2. can be used as sanding filler
   • sands well
   • Excellent high-build characteristics
   • Very good drying properties
   • ‎Long curing time

Application Instructions

Base Surface

Suitable base surfaces:

• sheet steel that has been cleaned, sanded and primed with Two-Part Wash Primer -LHV 043 000 A2- or One-Part Wash Primer -LVM 044 007/171 A2-, galvanized/electrolytically zinced sheet steel or soft aluminum
• Fine or non-sanded, thoroughly cleaned, original factory primer.
• Sanded factory paint or old paint (except TPA)
• Surfaces prepared with two-part polyester products and then sanded very fine.
• Cleaned and sanded UP-GF surfaces, free of separating agents

Pre-treatment of base surfaces:

• Carefully clean using Silicone Remover -LVM 020 000 A5- or Silicone Remover, Long -LVM 020 100 A5-.

• Then, sand.

• Use a suitable cleaning agent before reworking to ensure a clean and residue-free surface.

Use as interior color.

Mixture ratio:

2:1 by volume with:

• Two-Part HS Hardener -LHA 009 041 A3-
• Two-Part HS Hardener, Short -LHA 021 004 A3-
• Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
• Two-Part HS Hardener, Long -LHA 009 047 A3-
• Two-Part HS Hardener, Extra Long -LHA 009 048 A3-
• Two-Part HS Hardener, Special -LHA 009 049 A3-

Mixture ratio:

3:1 by volume with:

• Two-Part VHS Hardener, Short -LHA 009 050 A2-
• Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
• Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
• Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-

Processing time/pot life:

• Ready to spray 50 to 60 minutes at +20 ºC (68 ºF) (depending on the hardener used)

Additive:

• Mixed Filler Additive -LZS 811 000 A2-

Application type "coat"

• Processing viscosity 4 mm for +20 ºC, (68 ºF) German Industry Standardization 53211

Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 16 to 19 seconds

Adding 20 % HS hardener and 40 % VHS hardener at +20 ºC (68 ºF) material temperature

• Use a measuring stick to mix when pouring in the hardener.

• Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.4 mm.
• Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
• Set spray pressure (see manufacturer's information): "Compliant" to 1.5 to 3.0 bar.
• Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.

• Three spray applications are required to get a dry layer thickness of between 30 and 70 um.

More coats may be required, depending upon the color.

Note

When using as an interior color, overpainting the top coats does not apply.

Use as "wet-in-wet" filler

Mixture ratio:

2:1 by volume with:

• Two-Part HS Hardener -LHA 009 041 A3-
• Two-Part HS Hardener, Short -LHA 021 004 A3-
• Two-Part HS Hardener, Long -LHA 009 047 A3-
• Two-Part HS Hardener, Extra Long -LHA 009 048 A3-

Mixture ratio:

3:1 by volume with:

• Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
• Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
• Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-

Processing time/pot life:

• Ready to spray for 60 minutes at +20 ºC (68 ºF) (depending on the hardener used)

Additive:

• Mixed Filler Additive -LZS 811 000 A2-

Application type "coat"

• Processing viscosity 4 mm for +20 ºC (68 ºF), German Industry Standardization 53211

Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 16 to 19 seconds

Adding 20 to 30 % HS hardener and 40 to 50 % VHS hardener at +20 ºC (68 ºF) material temperature

• Use a measuring stick to mix when pouring in the hardener.

• Set spray nozzle (see manufacturer's information): "Compliant" 1.2 to 1.4 mm.
• Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
• Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
• Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.

• One to two spray applications are required to get a dry layer thickness of 30 um.

Drying time for "wet-in-wet" processing at +20 ºC (68 ºF) room temperature before applying the top coat:

• with water-based base paint for 30 to 120 minutes
• with two-part HS top coat for 15 to 120 minutes

Fast Point Repair System

Drying time for "wet-in-wet" processing at +20 ºC (68 ºF) room temperature before applying the top coat:

• with Two-Part HS Hardener, Extra Short -LHA 009 046 A2- for 15 minutes
• with Two-Part VHS Hardener, Short -LHA 009 050 A2- for 15 minutes

Adding Mixed Filler Additive -LZS 811 000 A2- 20 to 30 % HS hardener and 40 to 50 % VHS hardener at +20 ºC (68 ºF) material temperature.

• Use a measuring stick to mix when pouring in the additive.

Adding thinner 10 % Two-Part Thinner, Plus -LHA 014 000 A5- at +20 ºC (68 ºF) material temperature.

• Use a measuring stick to mix when pouring in the thinner.

Reworking

Can be painted over with:

• Water-based base paint and two-part HS clear coat
• Two-Part HS Top Coat

Use as Sanding Filler

Mixture ratio:

4:1 by volume with:

• Two-Part HS Hardener -LHA 009 041 A3-
• Two-Part HS Hardener, Short -LHA 021 004 A3-
• Two-Part HS Hardener, Extra Short -LHA 009 046 A2-
• Two-Part HS Hardener, Long -LHA 009 047 A3-
• Two-Part HS Hardener, Extra Long -LHA 009 048 A3-

Mixture ratio:

7:1 by volume with:

• Two-Part VHS Hardener, Short -LHA 009 050 A2-
• Two-Part VHS Hardener -LHA 009 051 A2-/-LVM 009 051 A5-
• Two-Part VHS Hardener, Long -LHA 009 052 A2-/-LHA 009 052 A3-
• Two-Part VHS Hardener, Extra Long -LHA 009 053 A2-

Processing time/pot life:

Ready to spray 90 to 120 minutes at +20 ºC (68 ºF) (depending on the hardener used).

Thinner:

• Two-Part Thinner -LVE 009 001 A5-
• Two-Part Thinner, Long -LVM 009 300 A2-
• Two-Part Thinner, Plus -LHA 014 000 A5-
• Two-Part Thinner, Special -LVM 009 200 A2/A5-

Application type "coat"

• Processing viscosity 4 mm for +20 ºC, (68 ºF) German Industry Standardization 53211

Processing viscosity 4 mm gravity feed spraygun "Compliant" and "HVLP" 18 to 20 seconds

Adding 15 % HS hardener and 25 % VHS hardener at +20 ºC (68 ºF) material temperature.

• Use a measuring stick to mix when pouring in the hardener.

• Set spray nozzle (see manufacturer's information): "Compliant" 1.3 to 1.7 mm.
• Set spray nozzle (see manufacturer's information): "HVLP" 1.3 to 1.5 mm.
• Set spray pressure (see manufacturer's information): "Compliant" to 2.0 to 2.5 bar.
• Set atomizing pressure (see manufacturer's information): "HVLP" 0.7 bar.
• Two to four spray applications are required (depending on spray nozzle used) to get a dry layer thickness of 200 um.

When air drying, the maximum dry layer thickness is 200 um.

When forced drying, the maximum dry layer thickness is 150 um.

When IR drying (bright colors), the maximum dry layer thickness is 150 um.

When IR drying (dark colors), the maximum dry layer thickness is 120 um.

Drying

The material can be sanded after 3 to 4 hours (layer thickness of 60 to 150 um after air drying at +20 ºC (68 ºF) room temperature).

If the applied layer thickness is between 150 and 200 um, the material should be allowed to dry over night and then sanded.

Final drying time with forced drying is a minimum of 5 to 15 minutes.

Forced drying at +60 ºC (140 ºF) object temperature for 30 to 35 minutes to 60 to 150 um

Final drying time for IR drying is a minimum of 5 to 10 minutes.

When IR drying (depending on layer thickness), use the medium-wave radiator for 15 minutes and the short-wave radiator for 10 minutes (of these, dry for 2 minutes at 50 % power and 8 minutes at 100 % power)

Further Processing

• Dry-sand with rotary sander and dust extraction. P400-500 grit sandpaper

• Wet-sand with P800-1000 grit sandpaper

Reworking

Can be painted over with:

• Water-based base paint and two-part HS clear coat
• Two-Part HS Top Coat

Special Instructions

Elastification for rigid and semi-rigid plastics:

• The base material must first be mixed with 15 % Elastic Additive -ALZ 011 001-.
• When engaged in "wet-in-wet" processing, use 2:1 two-part HS hardener and 30 % Mixed Filler Additive -LZS 811 000 A2-
• When engaged in "wet-in-wet" processing, use 3:1 two-part VHS hardener and 40 % Mixed Filler Additive -LZS 811 000 A2-
• When processing "as sanding filler", use 3:1 two-part HS hardener and 10 % thinner
• When processing "as sanding filler", use 4:1 two-part VHS hardener and 20 % thinner

• Before applying the water-based base paint, allow for 45 minutes of ventilation time at +20 ºC (68 ºF) room temperature.

• When using "sanding filler", the oven drying time is 45 minutes.
• Any faults in the base surface can be filled with two-part polyester filling paste. After drying and intermediate sanding, insulate the filler patches with two-part HS mixed filler.
• The best insulating effect, even with critical surfaces, is achieved with a medium layer of 60 to 120 um in 2 spray passes, with air-drying overnight, or oven/IR drying. With critical surfaces, fine preparation is required and the parts must be evenly filled.
• The Two-Part HS Vario Filler -LGF 786 004 A4- (gray) is recommended for insulating thermoplastic coatings.
• When air drying, maintaining a minimum temperature of +8º to 15 ºC (59 ºF) while using Two-Part HS Hardener, Extra Short -LHA 009 046 A2- is recommended.

Personal Protective Equipment:

• Note the safety data sheets
• Wear the personal protective equipment during application

Characteristics

Storage

The guaranteed shelf life of 24 months (48 months for mixed filler additive) from date of manufacture. Use no later than the date indicated on the label and store in original container at +20 ºC (68 ºF).