Volkswagen Tiguan Service and Repair Manual: Two-Part Fine Filling Paste, Flexible
Definition:
- Two-Part Fine Filling Paste, Flexible -LSP 787 100 A1-
Product Description
The Two-Part Fine Filling Paste, Flexible -LSP 787 100 A1- is a two component
filler paste with high filling characteristics.
The product does not collapse and has excellent adhesion on a multiple base
surfaces.
This filling paste is used especially for plastics:
Other Application Areas:
- For repair of plastic exterior body components where surface is damaged
with material removed (scratches, holes, rips), without being broken through
- For filling of KU-plastics, that were previously repaired with the
Plastic Repair Set -D 007 700-.
- For filling over a repair area to eliminate a mark
Application Instructions
Properties
- Constant, fine, creamy consistency
- High filling characteristics - no collapsing
- Hardens quickly
- Sands well
- Good adhesion on metal and plastic
Base Surface
Suitable base surfaces:
- Steel
- Galvanized sheet steel
- Aluminum
- On all cleaned and sanded plastics in vehicle area
- Fiberglass-reinforced plastics (UP-GF)
- Well-sanded old paint or factory paint
- Hardened two-part filler/two-part primers
Pre-treatment of base surfaces:
- Remove any grease and sand the surface.
- Bare metallic base surfaces are to be insulated with Two-Part Wash
Primer -LHV 043 000 A2- and then filled with Two-Part HS Performance Filler.
Sand the filler after drying.
- With UP-GF underbodies, clean components of any residual agents and sand
the surface.

- Clean once more using the Silicone Remover, Long -LVM 020 100 A5- or
Silicone Remover -LVM 020 000 A5- before reworking.

Reworking
Recommended structure:
- Fine filling paste by itself.
- Rework fine filling paste with Two-Part Fine Filling Paste -LSP 784 002
A2- or with Two-Part Spray Filling Paste -ALN 788 007- (except on galvanized
steel).
- Prime bare spots and filled areas with Two-Part Wash Primer -LHV 043 000
A2- and then fill with Two-Part HS Performance Filler.

- Then paint over with the top coat.
Note
Before filling, dry-sand the entire surface with P280-400 sandpaper.
Application Table
Mixing ratio |
2 to 3 % by weight |
Add hardener |
Two-Part Hardener
-LVM 018 00 A1- |
Pot life |
2 to 4 minutes at
+20 ºC (68 ºF) |
Drying time
(air drying at +20 ºC (68 ºF) room temperature) |
20 to 30 minutes |
Infrared
drying: |
|
|
short-wave |
approximately
three minutes (at 50 % output) |
|
middle-wave |
approximately five
minutes |
Sanding
compatibility |
Preliminary sanding |
Final sanding |
|
Wet |
as fine filling paste
P180 grit |
as fine filling paste
P320-P360 grit |
|
Dry |
as filling paste P80 grit, as
filling paste P120 grit |
as filling paste P120-P240
grit, as fine filling paste P280 grit |
Caution
This filling paste may not be applied to PVB (acid-hardening) adhesive
primers or one-part primers (for example, synthetic resin).
Application on thermoplastic or elastic coatings is also not possible. In
these cases, only apply filler paste to bare steel.
Note
- Before filling, dry-sand the entire surface with P280-320 sandpaper.
- Avoid using excessive hardener paste, to prevent it from bleeding
through, especially on daylight colors and light metallic colors.
- Reaction temperature at least +5 ºC (41 ºF).
Definition:
Two-Part Fine Filling Paste -LSP 784 002 A2-
Product Description
The two-part fine filling paste is a very fine thixotropic polyester filling
paste.
This filling paste is suitable for ...
Definition:
Two-Part Spray Filling Paste -ALN 788 007-
Product Description
The Two-Part Spray Filling Paste -ALN 788 007- is a two-part spray filling
paste used to level gross irregularities for v ...
See More:
Volkswagen Tiguan Owners Manual > Instrument cluster: Displays
Fig. 13 In the instrument cluster display:
A: Open engine hood, B: Open rear hatch, C: Open front driver side door, D: Open
rear passenger side door.
Depending on the vehicle model, different information may be shown
in the instrument cluster display ⇒ Fig. 11④ ⇒ Fig. 12④ .
Wa ...